Structural characterization of nanocrystalline SnO2 by X-ray and Raman spectroscopyстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:Tin dioxide nanocrystalline powders were prepared by precipitation of alpha-stannic acid followed by various thermal and chemical treatments, An original preparation via a colloidal solution step led to particles having a particular two-dimensional microstructure, The size of the crystallites was found to increase from 2 nm for as-prepared samples to 30 nm for samples annealed for 3.5 hr at 920 degrees C, The compounds were characterized by X-ray diffraction, scanning electron microscopy (SEM), and infrared and micro-Raman spectroscopy, As reported in the literature, the Raman spectral signature was found to change drastically with the size of the particles, A new spectral feature centered at about 500 cm(-1) was found for compounds prepared via the colloidal step and having typical sizes smaller than 4.5 nm, The powder Raman spectra are interpreted in terms of volume modes and surface modes, Their frequency evolution with crystallite size is discussed in terms of tensile surface stresses, (C) 1998 Academic Press.