Synthesis of Consolidated Carbon Nanomaterials by Spark Plasma Sinteringстатья
Информация о цитировании статьи получена из
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 29 июня 2022 г.
Аннотация:Few-layer graphene nanoflakes (GNFs) containing 8–10 graphene layers were treated at temperatures of 600–1800°C and pressures of 10–50 MPa by spark plasma sintering. At 600°С, the GNF powders did not consolidate; sintering with formation of pellets occurred at 1200–1800°С. As the temperature and pressure of sintering increased, the graphite structure became improved, and the number of carbon layers increased to 15–20; all the sintered samples were mesoporous.