Electroconductive and photoelectric properties of Pt/(100) β-Ga2O3 Schottky barrier diode based on Czochralski grown crystalстатья
- Авторы: Almaev Aleksei, Nikolaev Vladimir, Yakovlev Nikita, Butenko Pavel, Tsymbalov Alexander, Boiko Michael, Kopyev Viktor, Krymov Vladimir, Kushnarev Bogdan, Shapenkov Sevastian, Sharkov Michael, Zarichny Anton
- Журнал: Journal of Vacuum Science and Technology A
- Том: 42
- Номер: 4
- Год издания: 2024
- Издательство: AIP Publishing
- Местоположение издательства: United States
- DOI: 10.1116/6.0003618
- Аннотация: Pt/(100) β-Ga2O3 Schottky barrier diodes were fabricated using a plate cleaved from the crystal grown by Czochralski method. Their electroconductive and photoelectric characteristics were studied. The following values were obtained: the Schottky barrier height (1.69/1.62/1.74 eV), ideality coefficient (1.09/1.14), saturation current density (9.91 × 10–15 A/cm2), diode series resistance (7.98 kΩ), and net donor concentration [(1.8–2.4) × 1018 cm–3]. The diodes demonstrate a high rectification ratio of 1010 at an applied voltage of ± 1 V and a relatively low experimental value of the leakage current density ∼10–11 A/cm2. These structures are solar-blind and also capable of operating in self-powered mode. The diodes are highly sensitive to short-wave ultraviolet radiation with a wavelength λ ≤ 265 nm. The maximum values of responsivity (20.4 A/W), external quantum efficiency (1.2 × 104%), and detectivity (9.6 × 1015 Hz0.5 × cm × W–1) of diodes were registered under exposure to irradiation at λ = 210 nm and at applied voltage of −1 V. The responsivity and external quantum efficiency values in the self-powered operation mode were 12.3 A/W and 7.2 × 103%, respectively. The diodes showed low rise and decay times in self-powered operation mode for photodiode based on Ga2O3: 14 and 30 ms, respectively.