Rheological and rheokinetic properties of phosphazene-containing epoxy oligomersстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 9 ноября 2017 г.
Аннотация:The rheological and rheokinetic properties of a two-component binder consisting of epoxy-diane oligomers and the oligoepoxyphosphazenes PEO-1 (30 wt %) and PEO-2 (40 wt %) are studied. The viscosities of the initial oligomers at 40°C are 130 (PEO-1) and 270 (PEO-2) Pa s; the activation energies of viscous flow in the range 40–70°C are from 122 to 128 kJ/mol. The addition of equivalent amounts of curing agents, such as triethylenetetramine or iso-methyltetrahydrophthalic anhydride, reduces the initial viscosity of a composition, most strongly in the presence of the second curing agent (by a factor of 50–100). The activation energies of the cure process with triethylenetetramine in the range 45–95°C are 89 (PEO-1) and 125 (PEO-2) kJ/mol, and the gelation time at 55°C is 6 min for both oligomers. The time of gelation for the system PEO–iso-methyltetrahydrophthalic anhydride at 90°C is 475 min, and the glass-transition temperatures of the cured compositions are 238 (PEO-1) and 250°C (PEO-2), as evidenced by thermomechanical studies.